| 塑料名称(Polymer) |
PC/ABS |
| 厂商名称(Company) |
LG Chemical |
| 商品名称(Trade Name) |
Lupoy |
| 规格(Grade) |
GP-5008BF |
| 特征(Characteristic) |
防火,易流动 |
| 加工方法(Process Method) |
射出成型 |
| 物性名称 |
单位 |
测试方法 |
|
填充剂含量
Filler Content |
％ |
|
|
比重
Specific Gravity |
g/cm³ |
ASTM D792 |
1.20 |
融点
Melting Point |
℃ |
|
|
流动指数
MFR,(MI) |
g/10 min |
|
|
吸湿率@24h/23℃
Water Absorption |
％ |
|
|
成形收缩率
MD(Mold Shrinkage) |
％ |
ASTM D955 |
0.60 |
成形收缩率
TD(Mold Shrinkage) |
％ |
|
|
伸张断裂强度
Tensile Strength at Break |
MPa |
ASTM D638 |
52.00 |
伸张降伏强度
Tensile Strength at Yield |
MPa |
|
|
断裂伸张率
Tensile Elongation at Break |
％ |
ASTM D638 |
50.00 |
伸张弹性系数
Tensile Modulus |
MPa |
|
|
弯曲强度
Flexural Strength |
MPa |
ASTM D790 |
86.20 |
弯曲弹性系数
Flexural Modulus |
MPa |
ASTM D790 |
2450.00 |
艾氏耐冲击强度(缺口式)
Izod Impact Strength (notched) |
J/m |
ASTM D256 |
294.00 |
洛式硬度或秀尔硬度
Rockwell/Shore Hardenes |
|
|
|
热变形温度 0.46 MPa
Heat Distortion Temp |
℃ |
|
|
热变形温度 1.82 MPa
Heat Distortion Temp |
℃ |
ASTM D648 |
92.80 |
线膨胀系数10¯5
Coefficient of Linear Thermat Expansion |
mm/mm/℃ |
|
|
介电强度
Dielectric Strength |
kV/mm |
ASTM D149 |
38.00 |